沥青老化性能试验是评价沥青路面材料使用寿命的重要方法.通过采用旋转薄膜烘箱实验(RTFOT)后残留针入度、延度试验、动态剪切流变试验(DSR)方法,得到了荒漠地区橡胶改性沥青短期、长期老化规律.结果表明:RTFOT短期老化残留针入度:橡胶改性沥青>苯乙烯一丁二烯-苯乙烯嵌段共聚物(SBS)>克拉玛依(克)90号基质沥青;相位角δ:橡胶改性沥青DSR试验<SBS改性沥青<基质沥青.抗老化性能压力老化实验(PAV):橡胶改性沥青> SBS改性沥青>克90号基质沥青.研究得出掺入橡胶粉可明显提高沥青的抗变形、抗老化性能,可为废旧橡胶粉掺入路用沥青提供科学的理论支撑与技术指导.
Asphalt ageing test is an important method to evaluate the service life of asphalt pavement.By using the RTFOT residual penetration and delay test,DSR dynamic shear rheological test method the rubber modified asphalt short-term and long-term ageing rules in desertarea were obtained.The results showed that the rubber modified asphalt RTFOT short-term aging residual penetration>SBS modified asphalt residual penetration>G No.90 asphalt residual penetration;rubber modified asphalt DSR test phase angle Delta<SBS change sex asphalt<matrix asphalt phase angle Delta.Rubber modified asphalt PAV ageing properties>SBS modified asphalt anti-aging properties>G No.90 asphalt anti-ageing performance.The research showed that the addition of rubber powder could obviously improve the anti deformation and anti aging properties of asphalt.Research results could provide scientific theoretical support and technical guidance approach for the waste rubber powder mixed with asphalt.
[1] 贾钢.SBS改性沥青混合料低温性能试验分析与评价[J].公路与汽运,2008,1(1):83-85. JIA Gang.Experimental analysis and evaluation of low temperature performance of SBS modified asphalt mixture[J].Highways & Automotive Applications,2008,1(1):83-85.DOI:10.3969/j.issn.1671-2668.2008.01.028.
[2] 周进川,张智强,饶枭宇.SBS 改性沥青抗裂特性的SHRP 试验研究[J].重庆交通学院学报,2005,24(1):50-52. ZHOU Jinchuan,ZHANG Zhiqiang,RAO Xiaoyu.Study on SHRP SBS modified asphalts’ anti-cracking characteristics[J].Journal of Chongqing Jiaotong University,2005,24(1):50-52.DOI:10.3969/j.issn.1674-0696.2005.01.012.
[3] 李志栋,黄晓明.应用Superpave沥青标准预测低温开裂[J].中外公路,2004,24(3):100-103. LI Zhidong,HUANG Xiaoming.Application of superpave asphalt standard in forecasting the low temperature cracking[J].Journal of China & Foreign Highway,2004,24(3):100-103.DOI:10.3969/j.issn.1671-2579.2004.03.029
[4] 董瑞琨,孙立军.考虑老化的沥青结合料低温感温性指标[J].中国公路学报,2006,19(4):34-39. DONG Ruikun,SUN Lijun.Low temperature susceptibility lndexes of asphalt binder with different aging degree[J].China Journal of Highway and Transport,2006,19(4):34-39.DOI:10.3321/j.issn:1001-7372.2006.04.007.
[5] 封基良.沥青BBR小梁试验的流变分析[J].武汉理工大学学报(交通科学与工程版),2006,30(2):205-208. FENG Jiliang.Rheological analysis of asphalt tested by bending beam rheometer[J].Journal of Wuhan University of Technology(Transportation Science &Engineering),2006,30(2):205-208.DOI:10.3963/j.issn.2095-3844.2006.02.006.
[6] 朱春阳,杨毅,刘学建.不同标号沥青的弯曲梁流变试验对比分析研究[J].中外公路,2007,27(4):289-291. ZHU Chunyang,YANG Yi,LIU Xuejian.Comparison analysis and research of different grade asphalt with bending beams rheological Test[J].Journal of China & Foreign Highway,2007,27(4):289-291.DOI:10.3969/j.issn.1671-2579.2007.04.080.
[7] 詹小丽,张肖宁,卢亮,等.沥青临界开裂温度的研究[J].公路,2007,3:125-128. ZHAN Xiaoli,ZHANG Xiaoning,LU Liang,et al.A Study on critical cracking temperature of asphalt[J]. Highway,2007,3:125-128.DOI:10.3969/j.issn.0451-0712.2007.03.028.
[8] 苗其东,姚强,载鑫.浅论模拟沥青加热拌和老化的两种试验方法[J].石油沥青,2009,23(5):63-67. MIAO Qidong,YAO Qiang,ZAI Xin.Shallow theory of two kinds of test method with the simulate asphalt heating ageing of mixing[J].Petroleum Asphalt,2009,23(5):63-67.DOI:10.3969/j.issn.1006-7450.2009.05.014.
[9] ASPHALT INSTITUTE.Performance graded asphalt binder specification and testing superpaveries No.1(SP-1)[R].Lexington:Asphalt Institute,1994,36-48.