采用溶胶-凝胶法合成了LaKFeMoO6化合物的前驱体,在不同温度和不同氢气与氩气体积比的条件下合成了LaKFeMoO6.利用X射线衍射仪、振动样品磁强计对该化合物进行了晶体结构和磁学性能的表征. 结果表明,在800,830,850 ℃和不同的氢气体积分数下都可以形成双钙钛矿型化合物.然而在800 ℃烧结的样品其磁性受氢气体积分数的影响较小,在830,850 ℃烧结的样品受氢气体积分数的影响较大.
[1] KOBAYASHI K I, KIMURA T, SAWADA H. Room-temperature magnetoresistance in an oxide material with an ordered double-perovskite structure [J]. Nature 1998, 395.
[2] Sarma DD., Ray S., Nagarajan R., Majumdar S., Kumar A. Nalini G., Row TNG., Sampathkumaran EV.. Magnetoresistance in ordered and disordered double perovskite oxide, Sr2FeMoO6 [J]. Solid State Communications 2000, 9(9).
[3] Sarma DD., Saha-Dasgupta T., Ray S., Kumar A., Mahadevan P.. Electronic structure of Sr2FeMoO6 [J]. Physical review letters 2000, 12(12).
[4] Navarro J., Balcells L., Martinez B., Fontcuberta J., Frontera C.. Raising the Curie temperature in Sr2FeMoO6 double perovskites by electron doping - art. no. 092411 [J]. Physical Review.B.Condensed Matter 2001, 9(9).
[5] J. Kim, J.G. Sung, H.M. Yang. Effects of carrier doping on Curie temperature In double perovskite Ba_2FeMoO_6 [J]. Journal of Magnetism and Magnetic Materials 2005, 2(2).
[6] HUO Guoyan, LIU Shuang, WANG Ye. Structural and magnetic properties of the double perovskite LaKFeMoO6 compound [J]. J Alloy & Compds 2007, 433.
[7] LOBANOVSKII L S, TROYANCHUK I O, PUSHKAREV N V. Magnetoresistance effect in A2(FeMo)Ox double perovskits (A = Sr, Ca; 5.90≤x≤6.05) [J]. Physics of the Solid State 2001, 43.