对Bi 2223/ Ag多芯高温超导带材的焊接技术进行实验研究.焊接采用单轴方向不同压力下进行压接;另外在压接后,对不同压力压接下的样品进行热处理.实验结果表明:在77 K自场条件下,超导接头在压应力约为1.96×107 N/m2和热处理温度约为850 ℃时,得到焊接接头具有最高临界电流,其自场下临界电流约为带材临界电流的85%.
[1] Otto A., Masur L.J.. Multifilamentary Bi-2223 composite tapes made by a metallic precursor route [J]. IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee 1993, 1(1).
[2] Malozemoff A.P., Carter W., Fleshler S., Fritzemeier L., Li Q., Masur L., Miles P., Parker D., Parrella R., Podtburg E., Riley G.N. Jr., Rupich M., Scudiere J., Zhang W.. HTS wire at commercial performance levels [J]. IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee 1999, 2(2).
[3] Vase P., Flukiger R.. Current status of high-T_c wire [J]. Superconductor Science & Technology 2000, 7(7).
[4] Han Z., Bodin P.. Fabrication and characterisation of superconducting Bi-2223/Ag tapes with high critical current densities in km lengths [J]. IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee 1999, 2(2).
[5] Hayashi K., Hikata T., Kaneko T., Ueyama M., Mikumo A., Ayai N., Kobayashi S., Takei H., Sato K.. Development of Ag-sheathed Bi-2223 superconducting wires and theirapplications [J]. IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee 2001, 1(1).
[6] HASET, SHIBUTANI K, Hayashi S. Fabrication of superconductively jointed silver-sheathed Bi-2212 tape [J]. Cryogenics 1996, 36.
[7] KAZUFUMI, TANAKA, AKIRA NINOMIYA. Measurement of joint resistance of bi2223/Ag tapes using one-turn shorted coils [J]. IEEE Transactions on Applied Superconductivity 2001, 11.
[8] Jung Ho Kim, Jun Hyung Lim, Ho-Jin Kim, Jinho Joo, Cheol-Woong Yang, Wansoo Nah. Properties of resistive-and superconducting-joints in Bi-Pb-Sr-Ca-Cu-O tape [J]. IEEE Transactions on Applied Superconductivity: A Publication of the IEEE Superconductivity Committee 2001, 1 Pt.3(1 Pt.3).