LI Zhi-hua , XU Yan-hu . Buckling Failure Analysis in Plasma-sprayed Thermal Barrier Coatings[J]. Journal of Hebei University(Natural Science Edition), 2009 , 29(3) : 241 -244 . DOI: 10.3969/j.issn.1000-1565.2009.03.006

[1] 李志华, 李焕喜, 徐惠彬, 宫声凯. 热障涂层的残余应力分析 [J]. 北京航空航天大学学报 2004.doi:10.3969/j.issn.1001-5965.2004.03.020
[2] NISSLEY D M. Thermal barrier coating life modeling in gas turbine engines [A]. Cleveland:Ohio 1995.
[3] E. A. G. SHILLINGTON, D. R. CLARKE. SPALLING FAILURE OF A THERMAL BARRIER COATING ASSOCIATED WITH ALUMINUM DEPLETION IN THE BOND-COAT [J]. Acta materialia 1999, 4(4).
[4] Rabiei A., Evans A.G.. FAILURE MECHANISMS ASSOCIATED WITH THE THERMALLY GROWN OXIDE IN PLASMA-SPRAYED THERMAL BARRIER COATINGS [J]. Acta materialia 2000, 15(15).
[5] BOSE S, DEMASI-MARCIN J. Thermal barrier coating experience in gas turbine engine at Pratt&Whitney [A]. Cleveland:Ohio 1995.
[6] J. Thornton, D. Cookson, E. Pescott. The measurement of strains within the bulk of aged and as-sprayed thermal barrier coatings using synchrotron radiation [J]. Surface & Coatings Technology 1999, 0(0).
[7] V. Teixeira, M. Andritschky, W. Fischer, H. P. Buchkremer, D. Stover. Effects of deposition temperature and thermal cycling on residual stress state in zirconia-based thermal barrier coatings [J]. Surface & Coatings Technology 1999, 0(0).
[8] M V斯温, 郭景坤. 陶瓷的结构与性能 [M]. 北京:科学出版社 1998.
[9] A. G. Evans, D. R. Mumm, J. W. Hutchinson, G. H. Meier, F. S. Pettit. Mechanisms controlling the durability of thermal barrier coatings [J]. Progress in materials science 2001, 5(5).