Journal of Hebei University(Natural Science Edition) >

2017 , Vol. 37 >Issue 5: 464 - 470

DOI: https://doi.org/10.3969/j.issn.1000-1565.2017.05.004

On preparation and properties of composite nano-TiO2 transparent photocatalyst emulsion

  • LI Xiaowei ,
  • ZHAO Kaifeng ,
  • HU Xiaoxue ,
  • LU Qi ,
  • SUI Huidong ,
  • LI Jianwei ,
  • LIU Shuang
Expand
  • 1.Hebei Key Laboratory of Optic-electronic Information Materials, College of Physics Science and Technology, Hebei University, Baoding 071002, China; 2.College of Quality and Technology Supervision, Hebei University, Baoding 071002, China

Received date: 2017-07-01

  Online published: 2017-09-25

Fold

Abstract

Boron/fluoride co-doped nano TiO2 colorless and transparent hydrosol was synthesized by a novel complexation-controlled hydrolysis method at room temperature by using TiCl4, oxalic acid, NH3·H2O, ammonium fluoride, and boric acid etc as raw materials. The sample with the acid red 3R was studied by the photocatalytic degradation under simulated sunlight irradiation. To study the effects of reflux time, pH and-concentration and reaction conditions of the synthesis process and properties of the materials, the optimum preparation conditions were found out. The results show that when the doping amount is 0.003 mol/L, the pH value is 6, the reflux time is 15 min, the photocatalytic activity of doped nanometer TiO2 is the highest. The degradation rate of acid red 3R dye solution with the concentration of 50 mg/L was more than 98% after the sun exposure.

Key words： BF co-doped; nano TiO2 emulsion; hydrolysis method; photocatalysis

Cite this article

LI Xiaowei , ZHAO Kaifeng , HU Xiaoxue , LU Qi , SUI Huidong , LI Jianwei , LIU Shuang . On preparation and properties of composite nano-TiO2 transparent photocatalyst emulsion[J]. Journal of Hebei University(Natural Science Edition), 2017 , 37(5) : 464 -470 . DOI: 10.3969/j.issn.1000-1565.2017.05.004

References

[1] FUJISHIMA A, HONDA K. Electrochemical photolysis of water at a semiconductor electrode[J]. Nature, 1972,238(238): 37-38. DOI: 10.1038/238037a0
[2] FRANK S N, BARD A J. Heterogeneous photocatalytic oxidation of cyanide ion in aqueous solutions at titanium dioxide powder[J]. Journal of the American Chemical Society, 1977,99(1):303-304. DOI: 10.1021/ja00443a081.
[3] 李玉芳,伍小明. 纳米二氧化钛的制备及其在环保领域中的应用[J]. 精细化工原料及中间体,2008,9:1-8. LI Y F, WU X M. Preparation of nano titanium dioxide and its application in environmental protection[J]. Fine Chemical Industrial RawMaterials&Intermediates, 2008,9:1-8.
[4] 菅盘铭,夏亚穆,李德宏,等. 掺杂TiO2纳米粉的合成、表征及催化性能研究[J]. 催化学报,2001,22(2):161-164. JIAN P M, XIA Y M, LI D H, et al. Preparation, Characterization and Photocatalytic Activity of Doped TiO2 Nanopowders[J]. Chinese Journal of Catalysis, 2001,22(2):161-164.
[5] 邓谦,李明,蔡晴,等. 稀土/二氧化钛催化剂的制备和光催化消除气体污染物[J]. 中国稀土学报,2011,29(2):170-177. DENG Q, LI M, CAI Q, et al. Preparation of rare earth/titanium dioxide catalysts and photocatalytic elimination of gaseous pollutant[J]. Journal of the Chinese Society of Rare Earths, 2011,29(2):170-177.
[6] 郝仕油,吕灵莉,李群,等. 多孔Ce1-xNdxO2-y的微波引诱燃烧合成及其光催化性能研究[J]. 中国稀土学报,2011,29(3):295-302. HAO S Y, LV L L, LI Q, et al. Microwave-induced combustion synthesis and photocatalytic properties of porous Ce 1-x NdxO 2-y[J]. Journal of the Chinese Society of Rare Earths, 2011, 29(3): 295-302.
[7] 丁卉,张诺,戎非,等. 氮氟共掺杂二氧化钛薄膜的制备、表征及杀菌性能[J]. 无机材料学报,2011,26(5):517-522. DING H, ZHANG N, RONG F, et al. Preparation, characterization and bactericidal activity of N-F-codoped TiO2 film[J]. Journal of Inorganic Materials, 2011,26(5):517-522.
[8] ASAHI R, MOROKAWA T, OHWAKI T, et al. Photocatalytic material, photocatalytic article and method for their preparation[J]. At Be Ch Cy De Dk Es Fi Fr Gb Gr Le It Lu Mc Ni Pt Se, 2001,293(5528):267-271.
[9] CHOI W, TERMIN A, HOFFMANN M R. The role of metal ion dopants in quantum-sized TiO2: correlation between photoreactivity and charge carrier recombination dynamics[J]. Journal of Physical Chemistry, 1994,98(51):13669-13679. DOI: 10.1021/j100102a038.
[10] 黄东升,陈朝凤,李玉花,等. 铁、氮共掺杂二氧化钛粉末的制备及光催化活性[J]. 无机化学学报,2007,23(4):738-742. HUAN D S, CHEN C F, LI Y H, et al. Preparation and photocatalytic activity of TiO2 powder codoped with iron and nitrogen[J]. Chinese Journal of Inorganic Chemistry, 2007,23(4):738-742.
[11] 曹永强,龙绘锦,陈咏梅,等. 金红石/锐钛矿混晶结构的TiO2薄膜光催化活性[J]. 物理化学学报,2009,25(6):1088-1092. CAO Y Q, LONG H J, CHEN Y M, et al. Photocatalytic activity of TiO2 films with rutile/anatase mixed crystal Structures[J]. Acta Physico-Chimica Sinica, 2009,25(6):1088-1092.
[12] 李振华,刘中清,燕青芝,等. 合成温度对二氧化钛纳米管的影响[J]. 功能材料,2007,38(3):485-487. LI Z H, LIU Z Q, YAN Q Z, et al. The influence of synthesis temperature on the titania nanotube[J]. Journal of Functional Materials, 2007,38(3):485-487.
[13] 林明贤,赵高凌,汪建勋,等. 基板温度对常压化学气相沉积法制备TiO2复合薄膜性能的影响[J]. 硅酸盐学报,2007,35(11):1520-1525. DOI: 10.14062 /j.issn. 0454 -5648.2007.11.027 LIN M X, ZHAO G L, WANG J X, et al. Effect of substrate temperature on the propertles of TiO2 composite films deposited by atmospheric pressure chemical vapor deposition[J]. Journal of the Chinese Ceramic Society, 2007,35(11):1520-1525. DOI: 10.14062 /j.issn. 0454 -5648.2007.11.027
[14] 王积森,冯忠彬,孙金全,等. 纳米TiO2的光催化机理及其影响因素分析[J]. 微纳电子技术,2008,45(1):28-32. DOI:10.13250/j.cnki.wndz.2008.01.002 WANG J S, FENG Z B, SUN J Q, et al. Photocatalytic mechanism of nano-TiO2 and analysis on factors influencing its photocatalytic activity[J]. Micronanoelectronic Technology, 2008,45(1):28-32. DOI:10.13250/j.cnki.wndz.2008.01.002
[15] 孙俊英,孟大维,汪新星,等. 稀土元素掺杂对纳米TiO2光催化剂的影响及机理[J]. 材料导报,2007,21(F11):70-73.SUN J Y, MENG D W, WANG X X, et al. The influence of doping rare earth elements on nano-sized TiO2 and doping mechanism[J]. Materials Review, 2007,21(F11):70-73.
[16] 董素芳. 纳米TiO2光催化作用的影响因素及应用现状分析[J]. 硅酸盐通报,2005,24(4):85-88. DOI:10.16552/j.cnki.issn1001-1625.2005.04.020. DONG S F. Analysis on the present applications and factors affecting the photocatalysis of nano-TiO2[J]. Bulletin of the Chinese Ceramic Society, 2005,24(4):85-88. DOI:10.16552/j.cnki.issn1001-1625.2005.04.020.
[17] 陈瑞雪,太优一,俞欢,等.最小粒径钒/铁共掺杂纳米TiO2透明光触媒乳液的制备及其光催化性能[J].河北大学学报(自然科学版),2015,35(6):582-588.DOI:10.3969/j.issn.1000-1565.2015.06.005. CHEN R X,TAI Y Y,YU H,et al.Minimum particle diameter of the vanadium/iron co-doped nano-TiO2 transparent hydrosol at room temperature[J].Journal of Hebei University(Natural Science Edition),2015,35(6):582-588.DOI:10.3969/j.issn.1000-1565.2015.06.005.
[18] WANG Q, CHEN C C, ZHAO D, et al. Change of adsorption modes of dyes on flurinated TiO2 and its effect on photocatalytic degradation of dyes under visible irradiation[J]. Langmuir, 2008,24(14):7338-7345. DOI: 10.1021/la800313s.
[19] SACCO O, STOLLER M, VAIANO V, et al. Photocatalytic degradation of organic dyes under visible light on N-doped photocatalysts[J]. International Journal of Photoenergy, 2012,2012(4):518-542. DOI:10.1155/2012/626759.
[20] LU N, QUAN X, LI J Y, et al. Fabrication of boron-doped TiO2 nanotube array electrode and investigation of its photoelectrochemical capability[J]. Journal of Physical Chemistry C, 2007,111(32):11836-11842. DOI: 10.1021/jp071359d.
[21] LIU G, ZHAO Y N, SUN C H, et al. Synergistic effects of B/N doping on the visible-light photocatalytic activity of mesoporous TiO2[J]. Angewandte Chemie International Edition, 2008,47(24):4516-4520. DOI: 10.1002/ange.200705633.
Options
Outlines

/

〈 〉