A series of supported NiB nanocatalysts by an impregnation-reduction method were prepared and evaluated in the hydrogenation of cinnamic acid, and the effect of different supports(γ-Al2O3, SiO2, TiO2)on the catalytic activity and stability was investigated. It is found that the support γ-Al2O3 showed a better dispersion effect on nickel active species, and the NiB/γ-Al2O3 catalyst had a less loss of active species after several runs. The catalytic activity of NiB/γ-Al2O3 catalyst in the hydrogenation of cinnamic acid showed the best stability. Notably, the NiB/γ-Al2O3 catalyst was gradually abnormally increased after three runs, and the conversion of cinnamic acid was enhanced to 75.0% after three times, the selectivity of hydrogenation product was kept in 100%. It may be due to that active species NiB in channels of support are constantly exposed during the reaction process, and the support can effectively hinder the loss- DOI:10.3969/j.issn.1000-1565.2018.06.008载体对纳米NiB催化肉桂酸加氢催化活性与稳定性的影响韩雪1,2,冯文慧2,聂世琳2,兰兴旺2(1.河北省地质实验测试中心,河北 保定 071051;2.河北大学 化学与环境科学学院,河北 保定 071002)摘 要:采用浸渍-还原法制备负载型纳米NiB催化剂,以肉桂酸加氢反应为模型,考察载体(γ-Al2O3、SiO2、TiO2)对催化剂的催化活性和稳定性的影响.发现载体γ-Al2O3具有较好的分散镍活性组分的作用,在多次循环使用后催化剂活性组分流失较少.负载型NiB/γ-Al2O3催化剂在肉桂酸加氢反应中表现出较好的稳定性,此外,催化剂套用次数越多其活性反而越高,连续反应3次后肉桂酸的转化率可达75.0%,其加氢产物的选择性仍然保持在100%.通过系列表征,发现其最主要的原因可归为随着反应的不断进行载体孔道中的活性组分纳米NiB逐步暴露所致,更重要的是载体γ-Al2O3能够有效抑制活性组分的流失和团聚.关键词:γ-Al2O3;纳米NiB催化剂;稳定性;肉桂酸;加氢中图分类号:O643 文献标志码:A 文章编号:1000-1565(2018)06-0603-07Influence of supports on the catalytic activity and stability of NiB nanocatalyst in the hydrogenation of cinnamic acidHAN Xue1,2, FENG Wenhui2, NIE Shilin2, LAN Xingwang2(1. Hebei Geological Experimental Testing Center, Baoding 071051, China;2. College of Chemistry and Environmental Science, Hebei University, Baoding 071002, China)Abstract: A series of supported NiB nanocatalysts by an impregnation-reduction method were prepared and evaluated in the hydrogenation of cinnamic acid, and the effect of different supports(γ-Al2O3, SiO2, TiO2)on the catalytic activity and stability was investigated. It is found that the support γ-Al2O3 showed a better dispersion effect on nickel active species, and the NiB/γ-Al2O3 catalyst had a less loss of active species after several runs. The catalytic activity of NiB/γ-Al2O3 catalyst in the hydrogenation of cinnamic acid showed the best stability. Notably, the NiB/γ-Al2O3 catalyst was gradually abnormally increased after three runs, and the conversion of cinnamic acid was enhanced to 75.0% after three times, the selectivity of hydrogenation product was kept in 100%. It may be due to that active species NiB in channels of support are constantly exposed during the reaction process, and the support can effectively hinder the loss- 收稿日期:2018-07-01 基金项目:国家自然科学基金资助项目(21676068);河北省自然科学基金资助项目(B2018201118) 第一作者:韩雪(1983—),女,河北保定人,河北省地质实验测试中心工程师,主要从事绿色合成催化及分析测试研究.E-mail: yukixuer@163.com 通信作者:兰兴旺(1989—),男,河北唐山人,河北大学副教授,博士,主要从事纳米催化剂设计及二氧化碳转化反应和绿色合成研究.E-mail: hxlxw@sina.cn第6期韩雪等:载体对纳米NiB催化肉桂酸加氢催化活性与稳定性的影响and aggregation of active species.
HAN Xue
,
FENG Wenhui
,
NIE Shilin
,
LAN Xingwang
. Influence of supports on the catalytic activity and stability of NiB nanocatalyst in the hydrogenation of cinnamic acid[J]. Journal of Hebei University(Natural Science Edition), 2018
, 38(6)
: 603
-609
.
DOI: 10.3969/j.issn.1000-1565.2018.06.008
[1] UOZUMIY, ITO Y, OHTA H, et. al. Transfer hydrogenation of alkenes using Ni/Ru/Pt/Au heteroquatermetallicnanoparticle catalysts: sequential cooperation of multiple nano-metal species[J]. Chemical Communications, 2014, 50: 12123-12126. DOI: 10.1039/C4CC04559A.
[2] KEANE M A, PERRET N, WANG X D, et al. Selective hydrogenation of benzoic acid over Au supported on CeO2 and Ce0.62Zr0.38O2: Formation of benzyl alcohol[J]. Journal of Catalysis, 2014, 317: 114-125. DOI: https://doi.org/10.1016/j.jcat.2014.06.010.
[3] NEGOI A, TROTUS I T, STEINER O M, et al. Direct synthesis of sorbitol and glycerol from cellulose over ionic Ru/Magnetite nanoparticles in the absence of external hydrogen[J]. Chem Sus Chem, 2013, 6: 2090-2094. DOI: 10.1002/cssc.201300554.
[4] KUBO Y, FUJIWARA S, TAKANASHI N, et al. Boronatemicroparticle-supported nano-palladium and nano-gold catalysts for chemoselective hydrogenation of cinnamaldehyde in environmentally preferable solvents[J]. Green Chemistry, 2014, 16: 3230-3236. DOI: 10.1039/C4GC00383G.
[5] WU Q, XIONG JF, SHEN H, et al. Porous hierarchical nickelnanostructuresand theirapplication as a magnetically separable catalyst[J]. Journal of Materials Chemistry, 2012, 22:11927-11932. DOI: 10.1039/C2JM30361B.
[6] MONTINI T, SANTO V D, GALLO A, et al. H2 Production by renewables photoreforming on Pt-Au/TiO2 catalysts activated by reduction[J]. ChemSusChem, 2012, 5: 1800-1811. DOI: 10.1002/cssc.201200085.
[7] XIAO Q, YU J, YAN L, et al. Magnetically responsive core-shell Pd/Fe3O4@C composite catalysts for the hydrogenation of cinnamaldehyde[J]. Catalysis Letters, 2014, 144: 2065-2070. DOI: https://doi.org/10.1007/s10562-014-1328-z.
[8] DENG Y H, CAI Y, SUN Z K, et al. Multifunctional mesoporous composite microspheres with well-designed nanostructure: A highly integrated catalyst system[J]. Journal of the American Chemical Society, 2010, 132: 8466-8473. DOI: 10.1021/ja1025744.
[9] WANG W Y, YANG Y Q, LIU P L, et al. Synthesis of Ni-P-B amorphous nanoparticles with uniform size as a potential hydrodeoxygenation catalyst[J]. New Journal of Chemistry, 2015, 39: 813-816. DOI:10.1039/C4NJ01770F
[10] ZHAO F Y, MENG X C, CHENG H Y, et al. Selective hydrogenation of nitrobenzene to aniline in dense phase carbon dioxide over Ni/c-Al2O3: Significance of molecular interactions[J]. Journal of Catalysis, 2009, 264: 1-10. DOI: https://doi.org/10.1016/j.jcat.2009.03.008.
[11] CHEN L G, BAI G Y, I Y, et al. Selective synthesis of cis-2,6-dimethylpiperazine catalyzed by a Cu-Cr-Fe/g-Al2O3 catalyst[J]. Applied Catalysis A: General, 2004, 277: 253-258. DOI: https://doi.org/10.1016/j.apcata.2004.09.031.
[12] ZHAO F Y, LIN W W, CHENG H Y, et al. Deactivation of Ni/TiO2 catalyst in the hydrogenation of nitrobenzene in water and improvement in its stability by coating a layer of hydrophobic carbon[J]. Journal of Catalysis, 2012, 291: 149-154. DOI: https://doi.org/10.1016/j.jcat.2012.04.020
[13] LIANG G F, HE L M, CHENG H Y, et al. ZSM-5-supported multiply-twinned nickel particles: Formation, surface properties, and high catalytic performance in hydrolytic hydrogenation of cellulose[J]. Journal of Catalysis, 2015, 325: 79-86. DOI: https://doi.org/10.1016/j.jcat.2015.02.014.
[14] XIE G W, SUN W, LI W B. Synthesis and catalytic properties of amorphous Ni-Co-B alloy supported on carbon nanofibers[J]. Catalysis Communications, 2008, 10: 333-335. DOI: https://doi.org/10.1016/j.catcom.2008.09.013.
[15] LIU H, DENG J, LI W. Synthesis of nickel nanoparticles supported on boehmite for selective hydrogenation of p-nitrophenol and p-chloronitrobenzene[J]. Catalysis Letter, 2010, 137:261-266. DOI: https://doi.org/10.1007/s10562-010-0362-8.
[16] HARRAZ F A, EL-HOUT S E, KILLA H M, et al. Palladium nanoparticles stabilized by polyethylene glycol: Efficient, recyclable catalyst for hydrogenation of styrene and nitrobenzene[J]. Journal of Catalysis, 2012, 286:184-192. DOI: https://doi.org/10.1016/j.jcat.2011.11.001.
[17] LIAW B J, CHEN C H, CHEN Y Z. Hydrogenation of fructose over amorphous nano-catalysts of CoNiB and polymer-stabilized CoNiB[J]. Chemical Engineering Journal, 2010, 157: 140-145. DOI: https://doi.org/10.1016/j.cej.2009.11.020.
[18] LU H H, YIN H B, LIU Y M, et al. Influence of support on catalytic activity of Ni catalysts in p-nitrophenol hydrogenation to p-aminophenol[J]. Catalysis Communications, 2008, 10: 313-316. DOI: https://doi.org/10.1016/j.catcom.2008.09.015.
[19] FENG W H, DONG H X, NIU L B, et al. A novel Fe3O4@nSiO2@NiPd-PVP@mSiO2 multi-shell core-shell nanocomposite for cinnamic acid hydrogenation in water[J]. J. Mater. Chem. A, 2015, 3: 19807-19814. DOI: 10.1039/C5TA04894J.
[20] BAI G Y, DONG H X, ZHAO Z,et al. Effect of support and solvent on the activity and stability of NiCoB amorphous alloy in cinnamic acid hydrogenation[J]. RSC Adv., 2014, 4: 19800-19805. DOI:10.1039/C4RA01837K.
[21] 韩雪. 镍基纳米催化剂的制备及其在加氢反应中稳定性研究[D].保定:河北大学,2017. HAN X. Preparation of nickel-based nanocatalysts and their stabilities in hydrogenation reactions[D]. Baoding: Hebei University, 2017.