液晶p-BDAB的合成及其在不饱和聚酯树脂改性中的应用

doi:10.3969/j.issn.1000-1565.2010.02.015

摘要/Abstract

摘要： 以烯丙基溴、对羟基苯甲酸乙酯和联苯二酚为原料合成了二对烯丙基醚苯甲酸联苯二酚酯.用DSC,~1H-NMR,FTIR,POM 和XRD对其进行了表征, 结果表明:该化合物熔点为185 ℃,在178 ℃出现一个晶型转变,清亮点为278 ℃,为近晶型液晶.以此液晶化合物与普通不饱和聚酯(UP)共聚合固化,研究了液晶化合物用量对产物微观形态和性能的影响,结果表明:液晶化合物的加入可提高共聚物的抗冲击强度,但当液晶加入的质量分数超过8%时会产生相分离.

关键词: 联苯二酚酯, 液晶化合物, 不饱和聚酯

Abstract: A novel thermotropic liquid crystalline compound of p-biphenylene di-4-(allyloxy)benzoate (p-BDAB) was synthesized from allyl bromide,ethylparaben and 4,4-dihydroxybiphenyl.Its structure and liquid crystalline behavior were characterized by DSC,~1H-NMR,FTIR,POM and XRD.The results showed that this compound was smectic liquid crystal.The temperature range of liquid crystal was 185-278 ℃.The unsaturated polyester (UP) was improved by p-BDAB.The morphologic structure of UP improved with p-BDAB was investigated.The results showed that p-BDAB had reacted with UP.The p-BDAB was dispersed in the UP in the sea-island structure.UP had higher impact strength when the mass fraction of p-BDAB was about 8%,but the mass fraction was over 8%,the phase separation would occur and the impact strength would decrease.

Key words: dihydroxybipheny, liquid crystal, unsaturated polyester

中图分类号:

O631.5

张彩云,高俊刚,张媛媛. 液晶p-BDAB的合成及其在不饱和聚酯树脂改性中的应用[J]. 河北大学学报(自然科学版), 2010, 30(2): 180-184.

ZHANG Cai-yun,GAO Jun-gang,ZHANG Yuan-yuan. Synthesis of Liquid Crystalline p-BDAB and Its Modification Application on Unsaturated Polyester Resins[J]. Journal of Hebei University (Natural Science Edition), 2010, 30(2): 180-184.

参考文献

[1] 陈立新, 王汝敏, 蓝立文, 齐暑华, 刘郁扬, Chen Lixin, Wang Rumin, Lan Liwen, Qi Shuhua, Liu Yuyang. 含芳香酯基液晶基元环氧树脂的合成、表征及固化体系的研究 [J]. 玻璃钢/复合材料 2000.doi:10.3969/j.issn.1003-0999.2000.02.009
[2] 谭正德, 汤建武. 聚酯类热致性液晶的合成与其反应性共混的热性能改性 [J]. 湖南工程学院学报（自然科学版） 2004.doi:10.3969/j.issn.1671-119X.2004.04.020
[3] 刘晓丹, 高俊刚, 罗庆君, 张晓娜, 王玉阳, LIU Xiao-dan, GAO Jun-gang, LUO Qing-jun, ZHANG Xiao-na, WANG Yu-yang. 二对烯丙基醚苯甲酸对苯二酚酯液晶的合成与表征 [J]. 河北大学学报（自然科学版） 2007.doi:10.3969/j.issn.1000-1565.2007.01.016
[4] 李新贵, 黄美荣. 液晶高聚物的历史与进展 [J]. 高分子材料科学与工程 1993, 9(04).
[5] Huang YJ., Liang CM.. VOLUME SHRINKAGE CHARACTERISTICS IN THE CURE OF LOW-SHRINK UNSATURATED POLYESTER RESINS [J]. Polymer: The International Journal for the Science and Technology of Polymers 1996, 3(3).
[6] Zhang Bao-Long, Tang Guang-Liang, You Ying-Cai, Du Zong-Jie, Huang Ji-Fu. A Study on the Properties of Epoxy Resin Toughened by a Liquid Crystal-Type Oligomer [J]. Journal of Applied Polymer Science 1999, 1(1).
[7] HIETALAHTI KKARIN, SKRIFVARS MIKAEL, SUNDHOLM FRANCISKA. Solid-State ~13C Nuclear Magnetic Resonance Study of Cured, Unsaturated Polyester Resins [J]. Journal of Applied Polymer Science 1999, 4(4).
[8] BRAUN D, CHERDRON H, KER W T, 黄葆同. 聚合物合成和表征技术 [M]. 北京:科学出版社 1981.
[9] 高俊刚, 王勇, 侯桂香. 液晶p-PAEB原位改性不饱和聚酯树脂的结构形态和性能研究 [J]. 2006.
[10] 周其凤, 王新久. 液晶高分子 [M]. 北京:科学出版社 1994.

[1]	赵洪池,王耀辉,王畅,武永刚,宋洪赞. 5-[4-(2,3-环氧丙氧基)苯基]-10,15,20-三苯基卟啉的合成与表征[J]. 河北大学学报(自然科学版), 2013, 33(2): 148-153.
[2]	李新政,李晓苇,赖伟东,安文. 环境对光热敏微胶囊自由基聚合的影响[J]. 河北大学学报(自然科学版), 2012, 32(5): 467-471.
[3]	李丽霞,赵冬梅,范留彬,刘国栋. 玻璃态PS焓松弛β参数的热历史依赖性[J]. 河北大学学报(自然科学版), 2011, 31(6): 617-622.
[4]	姚宁,李元丰,宋建民,王云明. A_a-B_bC_c型缩聚反应中的悬吊链[J]. 河北大学学报(自然科学版), 2009, 29(6): 605-608.
[5]	程倩,徐建中. Ni(Ⅳ)引发苯乙烯在纤维素上接枝共聚合反应[J]. 河北大学学报(自然科学版), 2008, 28(3): 263-268.
[6]	张淑华,王素娟,邵书艳,姜春燕. 不饱和超支化聚(酰胺-酯)中双键的接枝改性[J]. 河北大学学报(自然科学版), 2007, 27(2): 170-173.
[7]	刘盈海,周玮琪,白利斌,张建平,张荣月,李胜贤. 镍(Ⅳ)引发甲基丙烯酸甲酯在碳黑表面接枝共聚合反应的研究[J]. 河北大学学报(自然科学版), 2006, 26(5): 489-495.
[8]	刘盈海,张建平,张荣月,史增谦,边瑞环. 苯乙烯可控阳离子聚合的新引发体系[J]. 河北大学学报(自然科学版), 2004, 24(6): 605-610.
[9]	史增谦,刘盈海,李艳香,杨兰英,李军波,王燕桓. 几种新型有机酸配体和FeCl2络合催化下的苯乙烯原子转移自由基聚合反应[J]. 河北大学学报(自然科学版), 2004, 24(2): 148-152.
[10]	姚兴芳,彭政,赵敏,巴信武. 四溴双酚A环氧树脂/二氨基二苯砜固化过程双玻璃化温度的形成机理[J]. 河北大学学报(自然科学版), 2003, 23(1): 41-44.
[11]	刘盈海,刘占军,刘晓辉,李军波,王红. 二羟基二过碘酸合镍(Ⅳ)钾氧化还原引发丙烯酸甲酯在尼龙6上的接枝共聚合反应[J]. 河北大学学报(自然科学版), 2003, 23(1): 29-33.
[12]	邓奎林,张艳哲,刘峥颢,刘盈海. 一氯乙酸/FeCl2·4H2O催化合成聚苯乙烯遥爪预聚物[J]. 河北大学学报(自然科学版), 2002, 22(2): 136-140.
[13]	栗明献,彭政,姚兴芳,赵敏,巴信武. 甲基丙烯酰氧基乙基三甲基氯化铵与甲基丙烯酸甲酯共聚物的合成与表征[J]. 河北大学学报(自然科学版), 2002, 22(1): 36-39.
[14]	洪晓钟,栗明献,赵敏,巴信武. 非线性Af-Bg型自由基交替共聚反应的凝胶网络结构表征[J]. 河北大学学报(自然科学版), 2001, 21(3): 273-276.
[15]	洪晓钟,巴信武,栗明献,赵玉梅,赵敏. 非线性Af-Bg型自由基交替共聚反应的统计理论[J]. 河北大学学报(自然科学版), 2001, 21(2): 134-137.