Preparation and properties of nano titanium dioxide/diatomite composite materials

doi:10.3969/j.issn.1000-1565.2015.01.006

Abstract

Abstract: The photocatalytic properties of nanosized TiO2/diatomite composites were studied with acid red 3R as waste water under solar light irradiation of 91700 uw/cm2 and ultraviolet irradiation of 499 uw/cm2. It was explored the best condition for nano TiO2 / diatomite composite material preparation in the experiment. The samples were characterized by SEM, XRD, EDS and IR analysis. The effect of pH, illumination time, and initial concentration of dye on catalytic performance were also investigated in detail. It showed that the best results was refluxed under acidic conditions for 75min, refluxed under neutral conditions 2h, TiO2 and diatomite material ratio 1:3 photocatalytic composite obtained. It can be found that the composite material exhibited better performance with longer illumination time and lower concentration of dye when the pH value of the solution was fixed at 3.

Key words: Nano Titanium Dioxide, Diatomite, Composite Material, Photocatalysis

CLC Number:

X703.1

DING Shiwen，Liu Tao，Li Tong，Guo Yang. Preparation and properties of nano titanium dioxide/diatomite composite materials[J]. Journal of Hebei University (Natural Science Edition), 2015, 35(1): 27-33.

References

1. Wu C H, Kuo C Y,Hong P K A．Effects of operational parameters On decolorisation of C.I.Reactive Black5 in UV/TiO2 system [J].Water Science & Technology,2011;63(5);1032-1036
2. Wang Cheng，Shi Huisheng，Li Yan. Synthesis and characteristics of natural zeolite supported　Fe3+-TiO2photoc　atalysts [J].Applied Surface Science,2011;257(15):6873-6877.
3. Fei Qi., Anna Moiseev, Joachim Deubener, Alfred Weber. Thermostable photocatalytically active TiO2 anatase nano　particles[J].Joumal of Nanoparticle Research,2011,13(3):1325-1334
4. 陈燕,宋新山,李洋,等.有序蘑菇状负载型纳米TiO2光催化剂制备[J].纳米技术与精密工程,2010;8(4):313-316CHEN Yan,SONG LI Xinshan, Yang,et al. Fabrication of Ordered Mushroom-Like Supported Nano TiO2 Photocatalyst[J].Nanotecnology and Precision Engineering, 2010;8(4):313-316
5. 徐志兵,孔学军,余锦龙等.负载型TiO2/硅藻土复合光催化剂的研究[J].稀有金属,2007,31(01):92-96.Xu Zhibing, Kong Xuejun, Yu Jinglong, et al. Study on TiO2/Diatomite Composite Photocatalyst[J]. CHINESE JOURNALOF RAREMETALS, 2007,31(01):92-96.
6. 李艳,王程,于开宁,等.多孔矿物/纳米TiO2复合体系光催化降解有机污染物研究进展[J].水处理技术,2009,35(03):10-12LI Yan, WANG Cheng, YU Kaining, et al. APPLICATION OF ADVANCED OXIDATION TECHNOLOGIES IN WASTEWATER TREATMENT[J]. TECHNOLOGY OF WATER TREATMENT,2009,35(03):10-12
7. 王利剑,郑水林,舒锋.硅藻土负载二氧化钛复合材料的制备与光催化性能[J].硅酸盐学报.34 (7):823-826.WANG Lijian，ZHENG Shuilin，SHU Feng, PREPARATION AND PHOTOCATALYTIC ACTIVITY OF TITANIA / DIATOMITE COMPOSITE[J]. JOURNAL OF THE CHINESE CERAMIC SOCIETY.34 (7):823-826.
8. 丁士文,张兴威,王利勇等.乳液浸渍法制备纳米TiO2/硅藻土复合材料[J].材料工程,2008,(10):50-52DING Shi wen,ZHANG Xingwei,WANG Li yong,et al. Preparation of Nano-TiO2/Diatomite Composite by Emulsion Dipping[J].JOURNAL OF MATERIALS ENGINEERING,2008,(10):50-52
9. Fang P Y. Wu J Q, ZHANG J T,et al. Preparation and photocatalytic performance of TiO2—Mounted diatomite composites by a hydrothermal method[J]. Journal of functional materials and devices. V01.16.No.1.
10. 王振兴,丁士文,张美红.高分散纳米二氧化钛混合晶体的合成、结构与光催化性能[J].无机化学学报,2005,21(3):437-440WANG Zhenxing,DING Shiwen,ZHANG Meihong. Synthesis,Structure and Photocatalysis of Nano-TiO2 Mixed Crystals[J].CHINESE JOURNAL OF INORGANIC CHEMISTRY,2005,21(3):437-440
11. 郑水林,王利剑,舒锋,等.酸浸和焙烧对硅藻土性能的影响[J].硅酸盐学报,2006,35(11):1382-1386ZHENG Shuilin,WANG Lijian,SHU Feng,et al. EFFECT OF CALCINING AND SULFURIC ACID TREATMENT ON PROPERTIES OF DIATOMITE[J].JOURNAL OF THE CHINESE CERAMIC SOCIETY,2006,35(11):1382-1386
12. 王利勇,韩媛媛,丁士文,等.光催化降解水中的酸性红3R及操作参数的影响[J].应用化工,2007,27(03):287-291 WANG Liyong,HAN Yuanyuan,DING Shi-wen,et al. Effect of operation parameter during photodegradation of acid red 3R[J]. Applied Chemical Industry,2007,27(03):287-291

[1]	LIU Xuemei, GUO Kexin, LI Jinhuan, LI Huimin, HU Ruohui. Synthesis and characterization of Waugh-type compounds containing quaternary ammonium cations [J]. Journal of Hebei University(Natural Science Edition), 2022, 42(3): 265-272.
[2]	LIU Haiyan, HAN Yamei, WANG Shan. Application of metal organic framework composites in solid phase extraction [J]. Journal of Hebei University(Natural Science Edition), 2022, 42(1): 44-59.
[3]	LIU Shuang'an, SHAN Yiyang, TANG Haoran, LI Meng, CHEN Jiaxin, YUAN Xiaoxian. Preparation and photocatalytic activity of electrospun europium-doped TiO₂ nanofibers [J]. Journal of Hebei University (Natural Science Edition), 2020, 40(3): 255-259.
[4]	ZHOU Lili, LIU Yanxia, LIU Le, FENG Xianqi. Fabrication and characterization of poly(N-isopropylacrylamide) /SiO₂ nanocomposite hydrogels [J]. Journal of Hebei University (Natural Science Edition), 2018, 38(5): 496-502.
[5]	LI Xiaowei,ZHAO Kaifeng,HU Xiaoxue,LU Qi,SUI Huidong,LI Jianwei, LIU Shuang. On preparation and properties of composite nano-TiO₂ transparent photocatalyst emulsion [J]. Journal of Hebei University (Natural Science Edition), 2017, 37(5): 464-470.
[6]	XIAO Junying,XU Jun,WU Chengjie,SUI Huidong,DING Wenge. Preparation and photocatalytic properties of the Cr-doped nano-TiO₂ emulsion [J]. Journal of Hebei University (Natural Science Edition), 2016, 36(4): 353-357.
[7]	WANG Mingkun,TAI Youyi,CUI Tong,LI Xiaowei,LI Ling. Preparation and photocatalysis performance of the sulfur-doped nano-TiO₂ transparent hydrosol [J]. Journal of Hebei University (Natural Science Edition), 2016, 36(2): 124-128.
[8]	CHEN Ruixue,TAI Youyi,YU Huan,HAO Wenzhuo,LI Ling. Minimum particle diameter of the vanadium/ iron co-doped nano-TiO2 transparent hydrosol at room temperature [J]. Journal of Hebei University (Natural Science Edition), 2015, 35(6): 582-588.
[9]	PANG Yanrong,CHEN Weiye,LIU Ran,TIAN Xiao,HU Jie. Acoustic emission behavior of defect evolution of fiber composites embedded with delamination [J]. Journal of Hebei University (Natural Science Edition), 2015, 35(4): 427-431.
[10]	LI Yajuan,ZHOU Wei,LIU Ran,LIANG Xiaomin,LI Zhiyuan. Acoustic emission monitoring for interlaminar crack of wind turbine blade composite [J]. Journal of Hebei University (Natural Science Edition), 2014, 34(2): 219-224.